https://elib.bsu.by/handle/123456789/340506| Title: | Исследование процесса формирования покрытий при электровзрывном напылении проводников, полученных методом компактирования порошковых материалов |
| Other Titles: | The Investigation of the Process of Formation Coatings by Electrical Explosion Spraying of Conductors Obtained by Powder Materials Compaction / Filyakov A.D., Chumachkov I.I., Pochetukha V.V. |
| Authors: | Филяков, А. Д. Чумачков, И. И. Почетуха, В. В. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2025 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 524-526. |
| Abstract: | Настоящая работа посвящена исследованию процесса формирования металлических покрытий методом электровзрывного напыления с использованием проводников, изготовленных путём компактирования порошковых материалов. В качестве напыляемого материала применялся медный порошок. Напыление осуществлялось на подложки из быстрорежущей инструментальной стали марки Р6М5 с использованием электровзрывной установки ЭВУ 60/10 М, оснащённой коаксиальными электродами. Полученные покрытия имели среднюю толщину порядка 50 мкм, отличались высокой адгезией к подложке, низкой пористостью. Экспериментально установлено, что при взрыве компактированного проводника формируется высокоскоростной ударный поток, способствующий интенсификации процесса осаждения частиц на подложку. Метод показал высокую эффективность при получении однородных и прочных металлических покрытий при минимальной подготовке исходного материала. В то же время необходимы дальнейшие исследования для более глубокого понимания физических механизмов, лежащих в основе процесса, и факторов, влияющих на морфологию и свойства покрытий |
| Abstract (in another language): | The present work is devoted to the study of the process of metal coating formation by the method of electrical explosion spraying using conductors produced by compacting powder materials. Copper powder (chemical composition mass % u min 99.5, As up to 0.003, Pb up to 0.05, O up to 0.2, Sb up to 0.005) with different dispersion was used as the sprayed material. Spraying was carried out on substrates made of high-speed tool steel grade R6M5 (GOST 19265-73) using an electrical explosive spraying machine, EVU 60/10 M, equipped with coaxial electrodes. The obtained coating had an average thickness of approximately 50 µm and was characterized by high adhesion to the substrate, low porosity. It was experimentally established that during the explosion of the compacted conductor, a high-speed shock flow is formed, contributing to the intensification of the process of particle deposition on the substrate. The method has shown high efficiency in obtaining homogeneous and durable metal coatings with minimal preparation of the source material. At the same time, further research is needed to better understand the physical mechanisms underlying the process and the factors influencing the morphology and properties of the coatings |
| Description: | Секция 5. Методы, оборудование, плазменные и радиационные технологии = Section 5. Methods, Equipment, Plasma and Radiation Technologies |
| URI: | https://elib.bsu.by/handle/123456789/340506 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2025. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 524-526.pdf | 119,12 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.