Структурные и оптические свойства углеродных нанотрубок, выращенных методом декомпозиции оксида углерода

Abstract

The information about the topography and particular structural features of carbon nanotubes (CNTs) was obtained by transmission electron microscopy and Raman spectroscopy using 514,5 nm excitation line from an Ar laser. Diameters of the nanotubes were calculated by the for­mulas obtained from different models using the values of RBM frequencies from Raman spectrum. The models taking into account interactions between the tubes in bundles give similar values of CNTs diameters. Based on analysis of the high-frequency spectral region, it was found that the samples contain a mixture of metallic and semiconductor nanotubes. Приведены результаты исследований топографии и структурных особенностей полученных путем газофазного разложения СО и Fe(CO)5 при высоком давлении и высокой температуре углеродных нанотрубок (УНТ) методом трансмиссионной электронной микроскопии и комбинационного рассеяния. Показано, что использование различных моделей расчетов диаметров УНТ из положения радиальных «дышащих» мод в спектре КР и учитывающих межтрубочные связи в связках УНТ приводит к близким значениям. На основании анализа высокочастотного диапазона спектра КР установлено, что исследуемые образцы содержат смесь металлических и полупроводниковых нанотрубок.