https://elib.bsu.by/handle/123456789/340565| Заглавие документа: | Разработка основ технологического процесса ремонта лопаток компрессора из стали 15Х16К5Н2МВФАБ с жаростойким алюминидным покрытием с помощью высокоинтенсивных импульсных электронных пучков |
| Другое заглавие: | Development of the Fundamentals of the Technological Process for Repairing Compressor Blades Made of 15X16K5N2MVFAB Steel with a Heat-Resistant Aluminide Coating using High-Intensity Pulsed Electron Beams / Bitsenko O.A., Shirokozhukhov A.V., Gromov A.N., Lobachev N.A. |
| Авторы: | Быценко, О. А. Широкожухов, А. В. Громов, А. Н. Лобачев, Н. А. |
| Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Дата публикации: | 2025 |
| Издатель: | Минск : БГУ |
| Библиографическое описание источника: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 228-230. |
| Аннотация: | В данной работе показана возможность использования облучения высокоинтенсивными импульсными электронными пучками для удаления эксплуатационного налета и деградированного жаростойкого алюминидного покрытия компрессорных лопаток из стали 15Х16К5Н2МВФАБ-Ш. Установлено, что для удаления покрытия и эксплуатационного налета необходимо реализовать облучение с плотностью 26-28 Дж/см2. При меньших плотностях энергии удаление материала не происходит. На основании данных металлографического исследования продемонстрировано, что после ремонта лопаток под новым покрытием наблюдается модифицированный слой глубиной до ~25 мкм, а дефектов покрытия не имеется. Микротвердость модифицированного слоя по сравнению основным материалом лопатки возросла на 40%. Результаты усталостных испытаний весьма неоднозначны, так как часть лопаток разрушилась до достижения контрольного уровня. Предполагается, что это связано с формированием остаточных растягивающих напряжений, которые в свою очередь и приводят к снижению предела выносливости при холодных испытаниях на усталость |
| Аннотация (на другом языке): | This paper shows the possibility of using high-intensity pulsed electron beam irradiation to remove operational plaque and degraded heat-resistant aluminide coating of compressor blades made of corrosion-resistant heat-resistant steel 15X16K5N2MVFAB. The blades of the compressor blades with a two-layer protective coating Ni-Cr-Al-Y + NiAl were used as objects of research. The irradiation was performed on an experimental experimental electron beam installation "GEZA-MMP" at various energy densities in the range from 20 J/cm2 to 40 J/cm2. The state of the material in the surface layers of the samples was studied by optical metallography, and microhardness was measured on a PMT-3 device at a load of 20 grams. In addition, fatigue tests were carried out according to the standard method based on tests of 2x10 6 cycles at room temperature (on magnetostrictive and electrodynamic vibration stands with a complex of measuring equipment). It has been established that in order to remove the coating and operational plaque, it is necessary to carry out irradiation with a density of 26-28 J/cm2. At lower energy densities, material removal does not occur. Based on the data of the metallographic study, it was demonstrated that after repairing the blades using the proposed technology, a modified layer with a depth of up to ~25 microns is observed under the new coating, and there are no defects in the new coating. The microhardness of the modified layer increased by 40% compared to the main blade material. According to the fatigue tests, three blades did not pass the control level, with destruction along the back of the pen. It is known that treatment with high-current pulsed electron beams almost always leads to the formation of residual tensile stresses and to a decrease in the endurance limit during cold fatigue tests. To remove the residual tensile stresses, diffusion vacuum annealing must be performed. Affiliation, full postal address, e-mail address (for each author if different) |
| Доп. сведения: | Секция 3. Влияние излучений на структуру и свойства материалов = Section 3. Radiation Influence on the Structure and Properties of Materials |
| URI документа: | https://elib.bsu.by/handle/123456789/340565 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Лицензия: | info:eu-repo/semantics/openAccess |
| Располагается в коллекциях: | 2025. Взаимодействие излучений с твердым телом |
Полный текст документа:
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| 228-230.pdf | 102,43 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.