https://elib.bsu.by/handle/123456789/340552| Title: | Облучение у-квантами 60Со структур DLC/полиимид |
| Other Titles: | Irradiation of DLC/Polyimide Structures with 60Co y-Quantums / Kharchenko A.A., Brinkevich D.I., Fedotova J.A., Zur I.A., Shmanay Y.Y., Movchan S.A., Remnev G.E., Linnik S.A., Buryi ЕЛ., S.B. Lastovskii V.V. |
| Authors: | Харченко, А. А. Бринкевич, Д. И. Федотова, Ю. А. Зур, И. А. Шманай, Е. Е. Мовчан, С. А. Ремнев, Г. Е. Линник, CA. Бурый, Е. Д. Ластовский, С. Б. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2025 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 190-192. |
| Abstract: | Методами измерения спектров пропускания исследованы облученные у-квантами 60Co дозой до 1 МГр структуры DLC/полиимид, сформированные методом сильноточного импульсного магнетронного распыления графита марки ГЛ-1. Мощность поглощенной дозы составляла 0.12 Гр/с. Показано, что существенные изменения спектров, наблюдавшиеся в области λ = 2700 - 3100 нм, обусловлены радиационно-индуцированными процессами на остаточных растворителях и побочных продуктах синтеза полиимида. Заметной трансформации структуры полимера, приводящей к снижению интенсивности полос поглощения в интервале длин волн 1600 - 2500 нм, не наблюдалось. Экспериментально установлено увеличение пропускания вблизи края поглощения полиимидной пленки и структур DLC/полиимид в процессе облучения у-квантами. Указанный эффект более выражен в структурах DLC/полиимид и обусловлен распадом метастабильных дефектов, сформированных в процессе изготовления полиимидной пленки и структур DLC/полиимид |
| Abstract (in another language): | DLC/polyimide structures irradiated with 60Co gamma rays at a dose of up to 1 MGy and formed by high-current pulsed magnetron sputtering of graphite of the brand GL-1 were studied using transmission spectrum measurement methods. The absorbed dose rate was 0.12 Gy/s. It is shown that significant changes in the spectra observed in the range of λ = 2700 - 3100 nm are due to radiation-induced processes on residual solvents and by-products of polyimide synthesis. There was no noticeable transformation of the polymer structure, leading to a decrease in the intensity of the absorption bands in the wavelength range of 1600 - 2500 nm. During gamma-ray irradiation, there was an increase in transmission near the absorption edge of the polyimide film and DLC/polyimide structures. This indicated effect is more pronounced in DLC/polyimide structures and is due to the decay of metastable defects formed during the manufacture of polyimide films and DLC/polyimide structures |
| Description: | Секция 2. Радиационные эффекты в твердом теле = Section 2. Radiation Effects in Solids |
| URI: | https://elib.bsu.by/handle/123456789/340552 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Sponsorship: | Работа выполнена в рамках ГПНИ «Фотоника и электроника для инноваций», подпрограмма «Микро- и наноэлектроника» (2021-2025), проект 3.2 (No 20212560). |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2025. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 190-192.pdf | 121,62 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.