https://elib.bsu.by/handle/123456789/340509| Заглавие документа: | Закономерности структурно-фазовых превращений и эволюции дефектной структуры циркониевого сплава Э110 с защитными хромовыми покрытиями при водородном воздействии и облучении |
| Другое заглавие: | Regularities of Structural-Phase Transformations and Evolution of Defect Structure of Zirconium Alloy E110 with Protective Chromium Coatings under Hydrogen Influence and Irradiation / Kruglyakov М.А., Kudiiarov V.N., Laptev R.S., Uglov V.V., Ivanov I.A., Koloberdin M.V. |
| Авторы: | Кругляков, М. А. Кудияров, В. Н. Лаптев, Р. С. Углов, В. В. Иванов, И. А. Колобердин, М. В. |
| Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Дата публикации: | 2025 |
| Издатель: | Минск : БГУ |
| Библиографическое описание источника: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 533-535. |
| Аннотация: | Осаждение хромовых покрытий (Cr) на поверхности циркониевого сплава Э110 (Zr1%Nb) снижает скорость проникновения водорода и замедляют его диффузию в объем сплава, что приводит к равномерному распределению водорода в объеме материала - повышение устойчивости к водородному охрупчиванию. Осаждение Cr на поверхность сплава Zr1%Nb уменьшает толщину зоны повреждения на 15-20% при облучении Kr+. На поверхности хромового покрытия и на границе раздела хром-цирконий энергия связи водорода и дефектов в 1.5-2 раза выше, чем в объеме циркония. В циркониевом сплаве Zr1%Nb при газофазном наводороживании в диапазоне температур 350-550 °C происходит интенсивное формирование дефектов вследствие формирования водород-вакансионных комплексов при растворении водорода в цирконии и образования гидридов в сплаве. Формирование защитного хромового покрытия на поверхности циркониевого сплава Zr1%Nb приводит к снижению концентрации дефектов в результате газофазного наводороживания и облучения по сравнению со сплавом без покрытия |
| Аннотация (на другом языке): | As a result of ex situ and in situ study of thermal and hydrogen impact processes, it was found that chromium coating on zirconium alloy Zr1%Nb contributes to the reduction of hydrogen absorption rate, which is 1.8 less compared to the material without protective coating. It is established that in the process of hydrogenation of zirconium alloy with chromium coating hydrogen diffuses into the volume of the material and is evenly distributed through the thickness of the sample which indicates the excellent protective qualities of this coating. A gradient of hydrogen distribution is observed in the volume of material without chromium coating after hydrogenation. It has been shown that the increase in hydrogen resistance of zirconium alloy with chromium coatings is in additional due to the presence of an incoherent interface and defects in its vicinity. Positron spectroscopy has shown that, in the case of chromium-coated zirconium materials after thermal treatment and hydrogenation, hydrogen is mainly localized at the Zr/Cr interface. Ex situ methods have determined that thermal and hydrogen impact results in the accumulation of dislocation-type defects in zirconium alloy due to the formation of hydrides. In addition, the peculiarities of microstructure changes in Cr-coated Zr1%Nb alloy under high-temperature hydrogenation and Kr-ion irradiation were investigated. A comprehensive analysis revealed that Cr coating reduces the thickness of the Kr+-radiation damage zone by 15-20% and decreases the density of radiation-induced defects compared to uncoated Zr1%Nb alloy. Moreover, Cr-coated samples exhibit a more uniform hydrogen distribution. According to first-principles calculations and positron annihilation spectroscopy, hydrogen-free dislocations predominate in the Cr-coated Zr1%Nb alloy after hydrogenation and irradiation. These findings emphasize the protective role of Cr coatings in mitigating radiation damage and hydrogen embrittlement in zirconium alloys |
| Доп. сведения: | Секция 5. Методы, оборудование, плазменные и радиационные технологии = Section 5. Methods, Equipment, Plasma and Radiation Technologies |
| URI документа: | https://elib.bsu.by/handle/123456789/340509 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Финансовая поддержка: | Работа выполнена в рамках Государственного задания «Наука» (научный проект № FSWW-2023-0005). |
| Лицензия: | info:eu-repo/semantics/openAccess |
| Располагается в коллекциях: | 2025. Взаимодействие излучений с твердым телом |
Полный текст документа:
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| 533-535.pdf | 101,96 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.