Please use this identifier to cite or link to this item:
https://elib.bsu.by/handle/123456789/313159| Title: | Электроосажденные покрытия медь – олово как катализаторы при электролизе воды в щелочных растворах |
| Other Titles: | Electrodeposited copper – tin coatings as catalysts for electrolysis of water in alkaline solutions / M. G. Galuza, T. N. Vorobyova |
| Authors: | Галуза, М. Г. Воробьева, Т. Н. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Химия |
| Issue Date: | 2024 |
| Publisher: | Минск : БГУ |
| Citation: | Журнал Белорусского государственного университета. Химия = Journal of the Belarusian State University. Chemistry. – 2024. – № 1. – С. 23-32 |
| Abstract: | Предложен этиленгликолевый электролит для осаждения на стальные электроды с никелевым подслоем покрытий Cu − Sn, содержащих 70 мас. % меди и включающих кристаллические фазы меди, олова и интерметаллида Cu6Sn5, твердого раствора электронного типа на базе соединения Cu5Sn, а также оксиды меди(II) и олова(IV) в следовых количествах. Определены изменения элементного и фазового состава покрытий в результате их прогрева при 250 и 400 °С и выщелачивания в 7,5 моль/дм3 растворе NaOH. Показано, что прогретые при 400 °С покрытия в процессе электролитического выделения как водорода, так и кислорода при щелочном электролизе воды обладают электрокаталитической активностью, превышающей активность используемого никелевого подслоя. Эти покрытия характеризуются коррозионной устойчивостью в 0,1 моль/дм3 растворе KOH, которая, судя по токам коррозии, превосходит устойчивость к коррозии электрода из никелированной стали. |
| Abstract (in another language): | Еthylene glycol electrolyte is proposed for Cu − Sn coatings deposition on steel electrodes with nickel sublayer. The coatings contain 70 wt. % of copper and include crystalline phases of copper, tin, intermetallic Cu6Sn5, electronic type solid solution based on Cu5Sn compound, and also copper(II) and tin(IV) oxides in trace quantities. Changes in the elemental and phase composition of the coatings were determined as a result of their heating at 250 and 400 °C and leaching in 7.5 mol/dm3 NaOH solution. It has been shown that coatings heated at 400 °C exhibit electrocatalytic activity in the process of electrolytic evolution of both hydrogen and oxygen during alkaline electrolysis of water, which exceeds the activity of nickel sublayer used. These same coatings are characterised by corrosion resistance in 0.1 mol/dm3 KOH solution, which, judging by the corrosion currents, exceeds the corrosion resistance of the nickel-plated steel electrode. |
| URI: | https://elib.bsu.by/handle/123456789/313159 |
| ISSN: | 2520-257X |
| Sponsorship: | Работа выполнена при финансовой поддержке Министерства образования Республики Беларусь (грант № 789/41). = The research was supported by the Ministry of Education of the Republic of Belarus (grant No. 789/41). |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2024, №1 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.