Пожалуйста, используйте этот идентификатор, чтобы цитировать или ссылаться на этот документ:
https://elib.bsu.by/handle/123456789/304327| Заглавие документа: | Исследование влияния рентгеновского излучения на коррозионную стойкость стирол-акриловых лакокрасочных покрытий |
| Другое заглавие: | Study of the influence of x-ray on the corrosion resistance of styrene-acryl paint coatings / N.G. Valko, V.M. Anishchik, D.I. Bogdevich |
| Авторы: | Валько, Н. Г. Анищик, В. М. Богдевич, Д. И. |
| Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Дата публикации: | 2023 |
| Издатель: | Минск : БГУ |
| Библиографическое описание источника: | Взаимодействие излучений с твердым телом : материалы 15-й Междунар. конф., Минск, Беларусь, 26-29 сент. 2023 г. / Белорус, гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2023. – С. 212-214. |
| Аннотация: | Представлены результаты исследования влияния рентгеновского излучения (0.07 нм), действующего в процессе отверждения, на защитные свойства стирол-акриловых лакокрасочных покрытий на водной основе ВД-АК-1179. Методом полярографического анализа исследована коррозионная стойкость покрытий в растворе NaCl. Анализ кривых анодного растворения показал, что у покрытий, отверждаемых в поле рентгеновского излучения плотность тока коррозии увеличивается, а потенциал полуволны уменьшается. Обнаруженные данные указывают на снижение коррозионной стойкости стирол-акриловых лакокрасочных покрытий на водной основе ВД-АК-1179 при отверждении их при воздействии рентгеновским излучением. Установлено, что с увеличением экспозиционной дозы коррозионная стойкость и адгезия облучаемых покрытий ухудшаются |
| Аннотация (на другом языке): | The effect of X-rays irradiation on curing water-based styrene-acrylic paint coatings have been carried out. It was study irradiation with exposure doses of 25, 50, 75, and 100 kR. Styrene-acrylic paints were irradiated with X-rays during curing. By the method of polarographic analysis the polarization curves of anodic dissolution of styrene-acrylic water-based paint coatings in 3 % sodium chloride solution were taken. The polarization curves were used for constructing Tafel’s curves in semilog coordinates. Using the Tafel’s curves the corrosion current density was found. It was established that a position of the curves of the irradiated water-based styrene-acrylic paint coatings shifted to the left to a less electropositive side compare with the curves of the non-irradiated paints. It was obtained that half-wave potentials of irradiated paints decreases and the corrosion current density increases. Observed data indicate decrease in corrosion resistance of irradiated paints. It is should be noted that the protective properties of water-based styrene-acrylic paint coatings irradiated with X-rays decreases with increasing of the exposure dose. The obtained relationships of the protective properties of styrene-acrylic paintwork irradiated during curing indicate the need to develop modes of irradiation of paintwork with lower energy |
| Доп. сведения: | Секция 3. Влияние излучений на структуру и свойства материалов = Section 3. Radiation influence on the structure and properties of materials |
| URI документа: | https://elib.bsu.by/handle/123456789/304327 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Лицензия: | info:eu-repo/semantics/openAccess |
| Располагается в коллекциях: | 2023. Взаимодействие излучений с твердым телом |