https://elib.bsu.by/handle/123456789/304250| Title: | Формирование и свойства АПУ/TiN покрытий на твердом сплаве |
| Other Titles: | Formation and properties of DLC/TiN coatings on hard alloy / Vadzim Chayeuski, Valery Zhylinski, Victor Kazachenko |
| Authors: | Чаевский, В. В. Жилинский, В. В. Казаченко, В. П. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2023 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 15-й Междунар. конф., Минск, Беларусь, 26-29 сент. 2023 г. / Белорус, гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2023. – С. 467-470. |
| Abstract: | В данной работе двухслойные покрытия из алмазоподобного углерода и нитрида титана (АПУ/TiN) были получены на фрезерных дереворежущих ножах из твердого сплава карбида вольфрама (WC – 3 мас.% Co) методом катодного вакуумно-дугового осаждения из паровой фазы (КИБ) и импульсным методом КИБ с графитовым катодом для осаждения слоев TiN и углерода, соответственно. С помощью методов сканирующей электронной микроскопии (СЭМ), энергодисперсионной рентгеновской спектроскопии (ЭДС), рентгеноструктурного анализа (РСА) и метода микроиндентирования были изучены структурно-механические свойства полученных покрытий, такие как, микроструктура, элементный, фазовый состав и микротвердость. АПУ/TiN покрытия состоят из двух отдельных слоев АПУ (верхний) и TiN (нижний). Верхний АПУ слой не смешивался с нижним TiN слоем. Измеренная толщина верхнего АПУ слоя составила ~198 нм, а толщина TiN слоя – ~2.39-2.75 мкм, при общей толщине покрытия ~2.59-2.95 мкм. Полученные покрытия характеризовались отдельными фазами γ-TiN, α-Ti, графита и синтетического алмаза. Показано, что АПУ/TiN покрытия обладают высокой твердостью 38.7-40.4 ГПа, что позволяет увеличить срок службы дереворежущего инструмента |
| Abstract (in another language): | In this work, the diamond-like carbon and titanium nitride (DLC/TiN) two-layer coatings were prepared on mill wood-cutter knives made from a cemented tungsten carbide (WC – 3 wt.% Co) using the cathodic vacuum arc physical vapor deposition (Arc-PVD) method and pulsed Arc-PVD method with a graphite cathode for the deposition of TiN and carbon layers, respectively. The structural and mechanical properties of the prepared coatings were studied, and different techniques, such as scanning electron microscope (SEM), Energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and microindentation technique investigated their microstructure, elemental and phases composition. The DLC/TiN coatings consist of two distinct layers of DLC (top) and TiN (bottom). The top layer of DLC has not been mixed with the bottom layer of TiN. The thickness of the top DLC layer was measured to be approximately 198 nm, while that of the TiN layer was measured to be around 2.39-2.75 μm, with a total coating thickness of roughly 2.59-2.95 µm. The prepared coatings were characterized by the distinct phases of c-TiN, α-Ti, graphite, and synthetic diamond. It had been demonstrated that the DLC/TiN coatings had a high hardness of 38.7-40.4 GPa, which can help to extend the wood-cutting tools' life |
| Description: | Секция 4. Наноматериалы: формирование и свойства при воздействии излучений = Section 4. Nanomaterials: formation and properties under the influence of radiation |
| URI: | https://elib.bsu.by/handle/123456789/304250 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2023. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 467-470.pdf | 370,86 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.