https://elib.bsu.by/handle/123456789/304247| Title: | Спектры комбинационного рассеяния радиационно-модифицированных алмазов и детонационных наноалмазов |
| Other Titles: | Raman spectra of radiation-modified diamonds and detonation nanodiamonds / А.А. Khomich, О.S. Кudryavtsev, М.V. Kozlova |
| Authors: | Хомич, А. А. Кудрявцев, О. С. Козлова, М. В. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2023 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 15-й Междунар. конф., Минск, Беларусь, 26-29 сент. 2023 г. / Белорус, гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2023. – С. 461-463. |
| Abstract: | В зависимости от степени радиационного повреждения и от температуры последующих высокотемпературных отжигов исследованы спектры комбинационного рассеяния света (КР) облученных быстрыми нейтронами или имплантированными ионами МэВ ионами радиационно-модифицированных природных и осажденных из газовой фазы (CVD) алмазов, а также химически очищенных детонационных наноалмазов. Показано, что в радиационно-поврежденных алмазах полоса «1640» состоит из нескольких пиков гауссовой формы, относительная интенсивность которых меняется как в зависимости от степени радиационного разупорядочения, так и от температуры последующего отжига. Обнаружено, что полоса «1640» в спектрах КР радиационно-поврежденных алмазов полностью отжигается при температурах выше 1000 °С, в то время как в детонационных наноалмазах отжиг до 1200 °С не оказывает существенного влияния на ее форму и интенсивность. Установлено, что спектральное положение полосы «1640» и ее интенсивность относительно бозонного пика может служить критерием критического радиационного повреждения алмаза |
| Abstract (in another language): | Raman spectra of irradiated with fast neutrons or MeV ion-implanted radiation-damaged natural and CVD diamonds and of chemically purified detonation nanodiamonds were studied depending on the degree of radiation damage and on the temperature of subsequent high-temperature annealing’s. The shape of the Raman spectra of the samples under study is determined by the effect of phonon confinement, which manifests itself in the form of an intense bosonic peak with a maximum near 400 cm-1 and a wide structural band up to 1300 cm-1, which repeats the spectrum of the density of phonon states of diamond. It is shown that the “1640” band in radiation-damaged diamonds consists of at least six Gaussian peaks with maxima at 1610, 1626, 1639, 1660, 1667 and 1692 cm-1, corresponding to the vibrations of various intrinsic radiation defects containing C=C bonds in their structure. The relative intensity of these peaks varies both depending on the degree of radiation damage and on the subsequent annealing temperature. It has been found that the “1640” band in the Raman spectra of radiation-damaged diamonds is completely annealed at temperatures above 1000°C and that the spectral position of the "1640" band and its intensity relative to the bosonic peak can serve as a criterion for critical radiation damage of a diamond. In the detonation nanodiamonds “1640” band is insensitive to annealing up to 1200°C and is due to the defects at the bulk of nanodiamonds |
| Description: | Секция 4. Наноматериалы: формирование и свойства при воздействии излучений = Section 4. Nanomaterials: formation and properties under the influence of radiation |
| URI: | https://elib.bsu.by/handle/123456789/304247 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2023. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 461-463.pdf | 426,33 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.