https://elib.bsu.by/handle/123456789/304229| Заглавие документа: | Повышение износостойкости штамповой стали Х12МФ путем комбинированной ионно-плазменной обработки |
| Другое заглавие: | Increasing the wear resistance of Cr12MoV die steel by combined ion-plasma treatment / Andrey Leonov, Yuliya Denisova, Vasily Tishchenko, Mikhail Savchuk |
| Авторы: | Леонов, А. А. Денисова, Ю. А. Тищенко, В. Н. Савчук, М. В. |
| Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Дата публикации: | 2023 |
| Издатель: | Минск : БГУ |
| Библиографическое описание источника: | Взаимодействие излучений с твердым телом : материалы 15-й Междунар. конф., Минск, Беларусь, 26-29 сент. 2023 г. / Белорус, гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2023. – С. 405-407. |
| Аннотация: | В работе представлены результаты исследования триботехнических свойств (износостойкости) штамповой стали Х12МФ, подвергнутой комбинированной ионно-плазменной обработке, включающей в себя ионно-плазменное азотирование и вакуумно-дуговое напыление на азотированный подслой нитридных покрытий на основе Ti и Cr. Азотирование проводили по двум режимам, при которых формировался «белый» нитридный слой и отсутствовал. Нитридный слой был толщиной 5-7 мкм, а толщина диффузионного слоя около 55-70 мкм. Было показано, что комбинированная обработка позволяет существенно снизить коэффициент трения до 0.159 – азотированные образцы с покрытием TiCrN (для стали Х12МФ коэффициент трения составлял 0.622), а также снизить параметр износа до 2.08×10 -7 мм3/Н·м – азотированные образцы с покрытием CrN (для стали Х12МФ параметр износа составлял 223×10 -7 мм3/Н·м) |
| Аннотация (на другом языке): | The paper presents the results of a study of the tribotechnical properties (wear resistance) of Cr12MoV cold work die steel subjected to combined ion-plasma treatment, including ion-plasma nitriding and vacuum-arc deposition on a nitrided sublayer of nitride coatings based on Ti and Cr. Nitriding was carried out in two modes, in which a "white" nitride layer was formed and was absent. The nitride layer was 5-7 µm thick, and the diffusion layer was about 55-70 µm thick. Nitrided samples were deposited with single-layer CrN and TiCrN coatings, as well as a 32-layer CrN/TiN coating. It was shown that combined treatment can significantly reduce the friction coefficient to 0.159 - nitrided samples with TiCrN coating (for Cr12MoV steel, the friction coefficient was 0.622), as well as reduce the wear parameter to 2.08×10 -7 mm3/N·m - nitrided samples with CrN coating (for Cr12MoV steel, the wear parameter was 223×10 -7 mm3/N·m). In addition, it was found that the combined treatment contributes to an increase in the microhardness of the samples compared to the initial and nitrided steel, and such a «coating-nitrided substrate» system has good adhesion |
| Доп. сведения: | Секция 4. Наноматериалы: формирование и свойства при воздействии излучений = Section 4. Nanomaterials: formation and properties under the influence of radiation |
| URI документа: | https://elib.bsu.by/handle/123456789/304229 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Финансовая поддержка: | Работа выполнена в рамках государственного задания Министерства науки и высшего образования Российской Федерации по теме № FWRM-2022-0001. |
| Лицензия: | info:eu-repo/semantics/openAccess |
| Располагается в коллекциях: | 2023. Взаимодействие излучений с твердым телом |
Полный текст документа:
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| 405-407.pdf | 372,77 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.