https://elib.bsu.by/handle/123456789/289990| Title: | ФОРМИРОВАНИЕ ОКТАКАЛЬЦИЙФОСФАТА ПРИ ВЗАИМОДЕЙСТВИИ КАРБОНАТА КАЛЬЦИЯ И МОНОКАЛЬЦИЙФОСФАТА МОНОГИДРАТА В ГАЛЬВАНОСТАТИЧЕСКИХ УСЛОВИЯХ |
| Other Titles: | FORMATION OF OCTACALIUM PHOSPHATE BY THE INTERACTION OF CALCIUM CARBONATE AND MONOCALCIUM PHOSPHATE MONOHYDRATE UNDER GALVANOSTATIC CONDITIONS / V. K. Krut’ko, A. E. Doroshenko, O. N. Musskaya, S. M. Rabchynski, A. I. Kulak |
| Authors: | Крутько, В. К. Дорошенко, А. Е. Мусская, О. Н. Рабчинский, С. М. Кулак, А. И. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Химия |
| Issue Date: | 2022 |
| Publisher: | Belaruskaya Navuka |
| Citation: | Proc Nat Acad Sci Belarus, Chem Series 2022;58(3):263-272. |
| Abstract: | National Research Center for Radiation Medicine Кальцийфосфатный композит октакальцийфосфат/кальцит получали в водной среде при pH 5–7 из суспензии CaCO3/Ca(H2PO4)2 в гальваностатическом режиме при плотности тока 20 мА/см2 в течение 20 мин. Высушивание при 80 °C без стадии созревания осадка приводило к получению порошка, состоящего из брушита, кальцита и малого количества октакальцийфосфата. Длительное созревание на воздухе (2 мес.) приводило к гидролитической трансформации брушита в октакальцийфосфат, стабилизированный кальцитом. Использование электрического тока позволило увеличить количество октакальцийфосфата в составе композитного порошка с морфологией пластинчатых розеток. Термообработка при 800 °C композитных порошков приводила к формированию α/β-трикальцийфосфата, β-пирофосфата кальция, гидроксиапатита и оксида кальция. |
| Abstract (in another language): | The calcium phosphate composite octacalcium phosphate / calcite was obtained at pH 5–7 from the CaCO3 /Ca(H2 PO4 )2 aqueous suspension in a galvanostatic mode at a current density of 20 mA/cm2 for 20 min. Drying at 80 °C without the precipitate maturation stage led to a powder formation consisting of brushite, calcite and a small amount of octacalcium phosphate. Prolonged maturation in air for 2 months led to the hydrolytic transformation of brushite into octacalcium phosphate stabilized by calcite. The use of electric current made it possible to increase the amount of octacalcium phosphate in the composite powder with the morphology of lamellar rosettes. Calcination at 800 °C of the composite powders led to the formation of α/β-tricalcium phosphate, β-calcium pyrophosphate, hydroxyapatite, and calcium oxide. |
| URI: | https://elib.bsu.by/handle/123456789/289990 |
| DOI: | 10.29235/1561-8331-2022-58-3-263-272 |
| Scopus: | 85138739166 |
| Sponsorship: | Acknowledgements. The work was financially supported by the SPSR “Chemical processes, reagents and technologies, bioregulators and bioorganic chemistry” under assignment 2.1.04.7 for 2021–2025. |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | Статьи химического факультета |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 736-1247-1-SM.pdf | 3,05 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.