https://elib.bsu.by/handle/123456789/271084| Title: | Латентные треки быстрых тяжелых ионов в нанокристаллическом Y4Al2O9 |
| Other Titles: | Swift heavy ion irradiation induced latent tracks in nanocrystalline Y4Al2O9 / A.K. Mutali, A.D. Ibrayeva, V.A. Skuratov, A.S. Sohatsky, Е. Korneeva, R.A. Rymzhanov, A. Janse van Vuuren, J.H. O’Connell, M.V. Zdorovets |
| Authors: | Мутали, А. К. Ибраева, А. Д. Скуратов, В. А. Сохацкий, А. С. Корнеева, Е. Рымжанов, Р. А. Янсе ван Вуурен, А. О’Коннелл, Ж. Г. Здоровец, М. В. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2021 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 14-й Междунар. конф., посвящ. 100-летию Белорус. гос. ун-та, Минск, Беларусь, 21-24 сент. 2021 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2021. – С. 182-185. |
| Abstract: | В работе представлены результаты исследования структурных изменений алюмоиттриевого оксида Y4Al2O9 (YAM), облученного в режиме одиночных треков ионами Bi и Xe в широком диапазоне удельных ионизационных потерь энергии, полученные с помощью просвечивающей и сканирующей просвечивающей электронной микроскопии высокого разрешения (С/ПЭМ). Установлено, что результатом воздействия высокоэнергетических тяжелых ионов является образование аморфных латентных треков, диаметр которых увеличивается с ростом потерь энергии на электронное торможение. На основе анализа зависимости размера треков от уровня ионизационных потерь энергии определено пороговое значение для образования треков в нанокристаллическом YAM, составляющее S et ~ 7-8 кэВ/нм |
| Abstract (in another language): | This work is aimed to study the swift heavy ion induced structural changes in nanostructured monoclinic yttrium aluminum oxide Y4Al2O9 (YAM) using high-resolution scanning/transmission electron microscopy (S/TEM). YAM with monoclinic crystallographic structure and space group P2 1 ⁄c (No. 14) is one of three crystalline phases in the Y-Al-O system and has a unique combination of high melting point (2020 ℃), low density (4.44 g/cm3), low high-temperature thermal conductivity (the minimum thermal conductivity is 1.13 W·m-1 K-1) and relative low Young’s modulus (191 GPa), which endure it as a candidate material for an inert matrix fuel hosts. YAM samples were irradiated with Bi and Xe ions having energies ranging from 156 to 714 MeV and electronic stopping powers - from 5 to 35 keV/nm at the IC-100 and U-400 FLNR JINR cyclotrons and the DC-60 cyclotron at the IRC INP. The ion fluence corresponding to the “individual tracks” regime was 5×10¹¹ cm⁻². S/TEM structural examinations showed that swift heavy ion induced latent tracks in YAM particles are continuous and amorphous. Ion track sizes larger than expected at the smallest energy loss for Xe ions and smaller track diameters at the highest energy loss for Bi ions are associated with the so-called "velocity effect". It is suggeste that the complexity of the crystal structure plays a significant role in formation of ion tracks in this material. The threshold value of electron stopping power for track formation in nanocrystalline YAM was found to be equal S et ~7–8 keV/nm |
| Description: | Секция 2. Радиационные эффекты в твердом теле = Section 2. Radiation Effects in Solids |
| URI: | https://elib.bsu.by/handle/123456789/271084 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Sponsorship: | Работа выполнена в рамках проекта ИРН (AP09058081) при поддержке Министерства образования и науки Республики Казахстан |
| Appears in Collections: | 2021. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 182-185.pdf | 421,48 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.