https://elib.bsu.by/handle/123456789/271081| Title: | Импульсная фотолюминесценция шпинели MgAl2O4, облученной тяжелыми ионами высоких энергий |
| Other Titles: | Pulsed photoluminescence of MgAl2O4 spinel irradiated with high energy heavy ions / M. Mamatova, V.A. Skuratov, A. Olejniczak, A.K. Dauletbekova, S.G. Giniyatova, A.T. Akilbekov |
| Authors: | Маматова, М. Скуратов, В. А. Олейничак, А. Даулетбекова, А. К. Гиниятова, Ш. Г. Акылбеков, А. Т. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2021 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 14-й Междунар. конф., посвящ. 100-летию Белорус. гос. ун-та, Минск, Беларусь, 21-24 сент. 2021 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2021. – С. 168-171. |
| Abstract: | Метод коррелированного по времени счета одиночных фотонов был использован для изучения кинетики фотолюминесценции монокристаллов алюмо-магниевой шпинели (MgAl2O4), облученной ионами Kr (100 МэВ), Ar (46 MэВ), Xe (148 МэВ) и Bi (710 МэВ). Люминесценция возбуждалась импульсным (~ 80 пс) лазерным излучением на длине волны 445 нм. Установлено, что спектральный состав фотолюминесценции радиационных дефектов, образованных в результате воздействия быстрых тяжелых ионов, представляет собой широкую неэлементарную полосу 500 - 750 нм с временами высвечивания 8 нс (500 нм), 8.9 нс (520 нм), 12 нс (620 нм) 13.7 нс (650 нм). Предполагается, что люминесценция может быть обусловлена излучательной рекомбинацией возбужденных состояний F+ - центров окраски и комплексами F+ - центр плюс примесь |
| Abstract (in another language): | Kinetic of photoluminescence of Magnesium Aluminate spinel (MgAl2O4) single crystals irradiated with high energy of Kr (100 MeV), Ar (46 MeV), Xe (148 MeV) and Bi (710 MeV) heavy ions in the fluence range from 10 10 to 2·10 13 cm-2 have been studied using the TCSPC (Time Correlated Single Photon Counting) technique. The luminescence was excited by a pulsed (~ 80 ps) laser light at a wavelength of 445 nm. As was found, the luminescence spectra of intact spinel consist of a sharp emission peak at 1.8 eV attributed to Cr 3+ impurity and a maximum at 2.35 eV ascribed to Mn2+ impurity. Photoluminescence spectra of samples, irradiated by swift heavy ions, have a broad non-elementary emission band in the spectral range at 500 – 750 nm, which indicating the radiation origin of the corresponding luminescence centers. Intensity of this band increases with the ion fluence, up to 10 13 cm-2 . It is assumed that luminescence can be caused by radiative recombination of excited states of F+ -color centers and F+ -color center plus impurity complexes. The emission decay times in this band for Xe ion irradiated spinel are ranged from 8 ns (500 nm) – to 13.7 ns (650 nm) |
| Description: | Секция 2. Радиационные эффекты в твердом теле = Section 2. Radiation Effects in Solids |
| URI: | https://elib.bsu.by/handle/123456789/271081 |
| ISSN: | 2663-9939 (Print) 2706-9060 (Online) |
| Sponsorship: | Работа выполнена в рамках проекта ИРН (АР09259669) при поддержке Министерства образования и науки Республики Казахстан |
| Appears in Collections: | 2021. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 168-171.pdf | 424,21 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.