Title: Thermodynamic behaviour and polymorphism of 1-butyl-3-methylimidazolium hexafluorophosphate composites with multi-walled carbon nanotubes
Authors: Liavitskaya, T.
Paulechka, E.
Blokhin, A.V.
Shevelyova, M.
Keywords: ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Химия
Issue Date: 2019
Publisher: Academic Press
Citation: J Chem Thermodyn 2019;131:262-268.
Abstract: Thermal behaviour of five (1-butyl-3-methylimidazolium hexafluorophosphate + multi-walled carbon nanotubes) materials was studied by adiabatic calorimetry over the temperature range (78–370) K. The samples differed by the nanophase content (0.11–0.92 mass fraction), preparative procedure, and appearance ranging from fluids to powders at room temperature. The specific heat capacity of the fluids was found to be an additive quantity of the heat capacities of the components for all phases, and the temperatures of phase transitions did not change relative to the bulk values for the ionic liquid. Evacuation of the contacting components was found to be a necessary step to reproducibly obtain the high-density fluids. However, no notable effect of the evacuation on thermal behaviour of the studied systems was detected. For the powder-like sample with the highest nanophase content, a sigmoidal heat capacity curve was observed. Based on this it was concluded that the internal diameter of the studied nanotubes was small enough to reveal a gradual transition from the crystal-like structures to the liquid-like ones instead of isothermal melting of the ionic liquid.
URI: https://elib.bsu.by/handle/123456789/261439
Scopus: 10.1016/j.jct.2018.11.006
metadata.dc.identifier.scopus: 85056779197
Appears in Collections:Статьи химического факультета

Files in This Item:
File Description SizeFormat 
статья.pdf1,91 MBAdobe PDFView/Open


PlumX

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.