https://elib.bsu.by/handle/123456789/233924| Title: | Влияние имплантации Ar, Kr и Xe на микроструктуру быстрозатвердевших сплавов Sn-Zn-Bi, легированных In |
| Other Titles: | Effect of Ar, Kr And Xe Implantation on the Microstructure of a Rapidly Solidfied Sn-Zn-Bi Alloys Doped by In / O.V. Gusakova, V.G. Shepelevich |
| Authors: | Гусакова, О. В. Шепелевич, В. Г. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2019 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids : материалы 13-й Междунар. конф., Минск, Беларусь, 30 сент. – 3 окт. 2019 г. / редкол.: В. В. Углов (отв. ред.) [и др.]. – Минск : БГУ, 2019. – С. 242-244. |
| Abstract: | Представлены результаты исследования влияния имплантации ионов Ar, Xe и Kr на микроструктуру быстрозатвердевшей фольги сплава Sn-Zn-Bi околоэвтектического состава, легированного In. Показано, что для всех сплавов имплантация приводит к ускоренному выделению включений Zn из пересыщенного твердого раствора. Обнаружено смещение границ зерен фольги сплава Sn – 5.2 мас. % Zn – 3.0 мас. % Bi -11 мас. % In, что приводит к образованию на поверхности ступеней субмикронных размеров. Обнаруженный эффект не наблюдается в однофазном сплаве, содержащем 3 мас. % In. Причиной смещения границ зерен может быть релаксация напряжений, существующих в исходном твердом растворе |
| Abstract (in another language): | The results of the study of the effect of implantation of Ar, Xe and Kr ions with an average energy of 1.0 and 1.75 MeV and a dose of 5×10 13 ions/cm 2 on the microstructure of the rapidly solidified foil of the near-eutectic Sn-Zn-Bi alloy doped with In are presented. It is shown that implantation leads to an accelerated segregation of zinc inclusions from the supersaturated solid solution and localization of inclusions at the grain boundary for all alloys. The grain structure of the alloy (Sn-Zn-Bi) - 3In is elongated coarse grains of tin-based solid solution and does not change when implanted with heavy ions of medium energy. The feature of changes in the microstructure of the surface of the Sn – 5,2 wt. % Zn – 3,0 wt. % Bi -11 wt. % In foil is the movement of grain boundaries, which leads to the formation of the surface steps of submicron sizes. This effect is not observed in a single-phase alloy containing 3 wt. % In. The reason for the grain boundaries movement can be the relaxation of internal stresses, stimulated both by the formation of point defects during implantation, and local heating of the surface. |
| Description: | Секция 3. Модификация свойств материалов = Section 3. Modification of Material Properties |
| URI: | http://elib.bsu.by/handle/123456789/233924 |
| ISSN: | 2663-9939 |
| Appears in Collections: | 2019. Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 242-244.pdf | 452,04 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.