https://elib.bsu.by/handle/123456789/233848| Title: | Изучение композиционного состава покрытий на основе W, сформированных на стали 40X методом ионно-ассистированного осаждения |
| Other Titles: | Studying the Composite Composition of Coatings Based on W, Formed on Steel 40X by Method Ion Assessed Depositionthe Title of the Report / Valentin Tul’ev |
| Authors: | Тульев, В. В. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2019 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids : материалы 13-й Междунар. конф., Минск, Беларусь, 30 сент. – 3 окт. 2019 г. / редкол.: В. В. Углов (отв. ред.) [и др.]. – Минск : БГУ, 2019. – С. 495-497. |
| Abstract: | Исследованы методом резерфордовского обратного рассеяния ионов гелия в сочетании с компьютерным моделированием состав и распределения элементов по глубине в приповерхностных слоях стали марки 40Х, полученных ионно-ассистируемым осаждением вольфрамсодержащих покрытий. Осаждение покрытий осуществлялось при ускоряющем напряжении 15 кВ, при интегральных потоках ассистирующих ионов (1−6)∙10 16 ион/см 2 . В рабочей камере в процессе осаждения покрытий поддерживался вакуум при давлении ~10 −2 Па. Установлено, что на поверхности образцов формируется покрытия толщиной ~30-50 нм со сложным композиционным составом. В состав покрытия входят атомы осажденного металла (2-15 ат.%), атомы технологических примесей углерода и кислорода, а также атомы железа из подложки. |
| Abstract (in another language): | Thin tungsten-containing films were applied on substrates of 40X steel using the method of the ion-assisted deposition in vacuum. This method allows to deposit of the coating on the surface of the sample and simultaneously irradiated with accelerated ions. The vacuum ion-arc plasma source of metals was used as implementation method. The source simultaneously generates positive ions and a neutral fraction from the material of the electrodes. Ion-assisted deposits were prepared using 15 kV accelerating voltage between sources and target. The density of ionic current at the deposition of the covering has changed in the range of 3 to 5 µA/cm2, and the ion flow has changed in the range of 1∙10 16 to 6∙10 16 cm-2. The deposition of the covering has occurred in a vacuum at a pressure ~10 –2 Pa in the working chamber. Rutherford back scattering and computer simulation RUMP code were applied to investigate the composition of the modified titanium surface. The research showed that the superficial structure is formed on titanium ~ 30-50 nm thick. The covering composition includes atoms of the deposited metal (2–15 at. %), atoms of technological impurity of carbon and oxygen (10–25 at. %), atoms of iron from the substrate. It has been determined that the penetration of metal atoms into the interior of the sample occurs as a result of radiation-stimulated diffusion, of iron atoms due to interdiffusion. The formation of the coating is affected by the sputtering of the surface of the formed structure. |
| Description: | Секция 5. Влияние излучений на структуру и свойства покрытий = Section 5. Radiation Influence on Coatings Structure and Properties |
| URI: | http://elib.bsu.by/handle/123456789/233848 |
| ISSN: | 2663-9939 |
| Appears in Collections: | 2019. Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 495-497.pdf | 371,14 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.