Термические свойства интерполиэлектролитных комплексов хитозана и сульфата ацетата целлюлозы

Abstract

Thermal degradation of chitosan (Cht), cellulose sulphate acetate (SAC) and interpolyelectrolyte complex (IPEC) Cht: SAC = 2:1 have been investigated by TG, DTG and DSC methods in nitrogen and air atmosphere. IPEC was prepared by mixing polymer solutions in the acetate buffer (0,16 M AcOH and 0,10 M AcONa). IPEC was established to show the existence of peak in DTG curve at 490 К and lack of the exothermal effect in DSC curve at 566 K. The thermal degradation curves of IPEC and mechanical blend of complying composition don't coincide. The thermal research results denote that the new compound is formed on the basis of Cht and SAC as a result of SAC sulphate groups and Cht amides interaction. The disappearance of the original polymers effects in DTG and DSC curves specifies IPEC as an individual compound. The thermostability of this product is higher than the additively calculated one. = Результаты термического исследования свидетельствуют об образовании на основе ХТЗ и САЦ нового соединения за счет взаимодействия сульфатных групп САЦ и аминогрупп ХТЗ, на индивидуальность которого указывает исчезновение на кривых ДТГ и ДСК эффектов, соответствующих исходным полимерам. Термостабильность полученного продукта значительно выше, чем аддитивно рассчитанная из характеристик индивидуальных полимеров.