Межфазное восстановление олеата меди борогидридом натрия

Abstract

The preparative peculiarities of the interphase reduction of copper oleate by sodium borohydride were investigated. It was shown the reaction products are formed as sediment or colloidal dispersion in the one phase of hexane/water or hexane/ethanol two-phase systems and correspond to the mixture of the metallic copper and copper (I) oxide. The average size of the coherent scattering re- gions are 5,5÷8,0 nm. The UV-spectra of the prepared colloidal dispersion are characterized by maximum at 560÷590 nm and suffi- ciently strong adsorption at 800 nm. The aging of the colloidal dispersions were studied by liquid chromatography, UV- and NMR- spectroscopy on protons. It was shown the dispersion’s aging is accompanied by both low temperature hydrogenation of the oleic acid double bond and copper stearate precipitation. The generated copper stearate is reversibly reduced by sodium borohydride and colloidal dispersion of the metallic copper and copper (I) oxide is formed. = Изучены препаративные возможности межфазного восстановления олеата меди борогидридом натрия. Показано, что в зависимости от концентрации и соотношения реагентов продукты реакции образуются в виде коллоидных растворов или осадков в одной из фаз двухфазной системы гексан/вода (гексан/этиловый спирт) и представляют собой смесь металлической меди и оксида меди(I). Размер областей когерентного рассеяния продуктов реакции составляет 5,5÷8,0 нм. Оптические спектры полученных коллоидных растворов характеризуются максимумом при 560÷590 нм и достаточно сильным поглощением в области 800 нм. Методами жидкостной хроматографии, оптической и ПМР-спектроскопии изучен процесс старения коллоидных растворов, сопровождающийся низкотемпературным гидрированием двойной связи олеиновой кислоты, образуя осадок – стеарат меди, который обратимо восстанавливается борогидридом натрия с образованием коллоидного раствора металлической меди и оксида меди(I).