Синтез и термопревращения двойных аммонийсодержащих полифосфатов никеля и кобальта

Abstract

New technique of obtaining double ammonium-containing nickel and cobalt polyphosphates, promising flame retardant additives to polyamides, by reactions with NH4PO3 was developed. Thermal behaviour of synthesised rhombohedral and orthorhombic MNH4(PO3)3 (M = Ni, Co), Ni(NH4)2(PO3)4·2H2O, monoclinic M(NH4)2(PO3)4 (M = Ni, Co) was studied within the temperature range of 20÷600 °C. It was found that all anhydrous compounds decompose at the temperature above 350 °C. Orthorhombic MNH4(PO3)3, cyclotetraphosphate M2P4O12 and polyphosphoric acids are condensed products of heating M(NH4)2(PO3)4. Finale products of heating MNH4(PO3)3 are M2P4O12 and polyphosphoric acids. The obtained results show that all investigated double polyphosphates can be used as additives to polyamides. = Разработан новый способ получения двойных аммонийсодержащих полифосфатов никеля и кобальта путем термического взаимодействия соединений указанных металлов с NH4PO3. Термическое разложение синтезированных ромбоэдрических и орторомбических MNH4(PO3)3 (M = Ni, Co), Ni(NH4)2(PO3)4·2H2O, моноклинных M(NH4)2(PO3)4 (M = Ni, Co) изучено в интервале температур 20÷600 °C. Установлено, что безводные соединения начинают разлагаться при температурах выше 350 °C, что позволяет использовать их в качестве специальных добавок к полиамиду-6. При этом конденсированными продуктами терморазложения M(NH4)2(PO3)4 являются орторомбические MNH4(PO3)3, циклотетрафосфаты M2P4O12 и полифосфорные кислоты. Показано, что конечный продукт нагревания MNH4(PO3)3 – M2P4O12 и полифосфорные кислоты. Термическая стабильность синтезированных КФМА хорошо коррелирует с составом и строением соединений и позволяет вводить их в полимерные композиции на основе полиамида-6 в качестве специальных добавок.