Химическое осаждение пленок Ni-W и Ni-P на алюминий как способ защиты алюминия от коррозии

Abstract

The method of corrosion protection of aluminium in sodium chloride solution has been suggested providing electroless deposition of Ni–W–P (nickel – 87,3 at. %, tungsten – 7,8 at. %, phosphorus – 4,9 at. %) and Ni–P (nickel – to 77 at. %, phosphorus – to 23 at. %) alloys from hypophosphite-citrate-glycine (Ni–W–P) and hypophosphite-acetate (Ni–P) electrolytes. Ni–W–P coatings 1,0÷1,2 μm thick consisting of close-packed grains about 1 μm in size appeared to be especially effective in retarding aluminium corrosion. The important property of protective films under investigation is their nonporosity in spite of a rather small thickness. A sufficient displacement of the anodic oxidation potential (1000 mV to the positive side) and a decrease in the current of anodic dissolution for more than one order when aluminium samples are covered with these coatings has been established. = Предложен метод защиты алюминия от коррозии в водных растворах хлорида натрия путем химического осаждения коррозионно-устойчивых покрытий на основе сплава Ni–W–P (никель – 87,3 ат. %, вольфрам – 7,8 ат. % и фосфор – 4,9 ат. %), полученного из гипофосфитно-цитратно-глициновых растворов и сплава Ni–P (никель – до 77 ат. % и фосфор – до 23 ат. %), осажденного из гипофосфитно-ацетатного электролита. Показано, что наилучшие защитные свойства проявляют пленки сплава Ni–W–P толщиной 1,0÷1,2 мкм, состоящие из плотно упакованных зерен со средним размером зерен 1 мкм. Эффективность их защитного действия почти вдвое выше, чем у пленок Ni–P. Установлено, что наличие защитных пленок Ni–W–P обеспечивает сдвиг потенциала начала анодного растворения алюминия в положительную область почти на 1000 мВ и уменьшение тока анодного растворения более чем на порядок.