Влияние оксидных добавок с перовскитоподобной структурой на микроструктуру и некоторые свойства магний-цинкового феррита

Abstract

In this work the effect of complex oxide dopes, such as La0,5Li1,5NiOx, Sr1,6Nd0,4NiO4–δ, Sr3Bi0,6Ni1,2O6–δ on the microstructure and microwave absorbing properties in the frequency range of 7,0÷8,5 GHz of the Mg0,43Zn0,57Fe1,98O4 ferrite has been studied. Sr1,6Nd0,4NiO4–δ, Sr3Bi0,6Ni1,2O6–δ dopes, coating Mg – Zn ferrite particles, restrict their growth and can act as bridges between ferrite ones. On the contrary, La0,5Li1,5NiOx dope forms solid solution. The maximum value of attenuation of 14,6 dB at 7,0 GHz for Sr3Bi0,6Ni1,2O6–δ doped composites is obtained. However, the minimum point is observed for La0,5Li1,5NiOx and equals – 4,32 dB at 8,5 GHz. = Изучено влияние сложнооксидных добавок La0,5Li1,5NiOx, Sr1,6Nd0,4NiO4–δ, Sr3Bi0,6Ni1,2O6–δ на микроструктуру и поглощающие свойства магний-цинкового феррита Mg0,43Zn0,57Fe1,98O4 в частотном диапазоне 7,0÷8,5 ГГц. Добавки Sr1,6Nd0,4NiO4–δ и Sr3Bi0,6Ni1,2O6–δ, располагаясь на поверхности ферритных зерен, препятствуют их дальнейшему росту в процессе термообработки и выступают в качестве электропроводящего мостика между ними. Добавка La0,5Li1,5NiOx вошла в структуру зерна, образовав твердый раствор. Максимальное значение отражения наблюдалось для композита с добавкой Sr3Bi0,6Ni1,2O6–δ при 7,0 ГГц и составило величину 14,6 дБ, в то же время минимальная величина отражения зафиксирована для композита с добавкой La0,5Li1,5NiOx – 4,32 дБ при 8,5 ГГц.