Магнитная структура твердых растворов Sr (0, 78) Y (0, 22) Co (1-х) Fe (x) O (3-d)

Abstract

The system Sr0,78Y0,22Co1–xFexO3–d has been studied by X-ray and neutron diffraction methods as well as magnetization measurements. Crystal structure of compositions with х ≤ 0,12 is described by the Immm space group based on the 2ар·2ар·4ар- unit cell. The crystal structure of these compositions includes alternating layers of CoO6 and CoO4,5. Magnetic structure is determined as anti-ferromagnetic of G-type. Magnetic moments in the СоО6 layers are much larger than those in the СоО4,5 ones. Small ferromagnetic component (0,2 μB/Сo) is observed by magnetic measurements in the x = 0 composition below TN ≈ 350 К. Doping with Fe ions leads to the ferromagnetic component suppression and sharp increase of average magnetic moment in the both layers. The ferromagnetic component is supposed to result from the non-collinearity of magnetic moments which may be caused by a competition between positive and negative exchange interactions as well as magnetic anisotropy. = Приведены результаты нейтроно- и рентгенографических исследований, измерений намагниченности и упругих свойств системы кобальтитов Sr0,78Y0,22Co1–xFexO3–d. Кристаллическая структура составов с х ≤ 0,12 была описана пространственной группой Immm на базе 2ар·2ар·4ар-элементарной ячейки. В составе с x = 0 с помощью магнитных измерений обнаружена небольшая ферромагнитная компонента (0,2 μВ/Сo) ниже TN ≈ 350 К. Предполагается, что ферромагнитная компонента является следствием неколлинеарности магнитных моментов, что может быть обусловлено конкуренцией обменных взаимодействий разного знака и магнитной анизотропии.