https://elib.bsu.by/handle/123456789/340597| Title: | Модификация заэвтектического силумина импульсным электронным пучком |
| Other Titles: | Modification of Hypereutectic Silumin by Impulse Electronic Beam / Rygina M.E., Koval N.N., Ivanov Yu.F., Moskvin P.V., Prudnikov A.N., Vorobyov M.S. |
| Authors: | Рыгина, М. Е. Коваль, Н. Н. Иванов, Ю. Ф. Москвин, П. В. Прудников, А. Н. Воробьёв, М. С. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2025 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 329-331. |
| Abstract: | В работе представлены результаты механических испытаний образцов заэвтектического силумина до и после модификации импульсным электронным пучком субмиллисекундной длительности воздействия в режиме ступенчатой обработки (со снижением плотности энергии пучка электронов) и при постоянной плотности энергии пучка электронов. При воздействии на образец на поверхности в режиме снижения плотности энергии пучка электронов происходит увеличение предела прочности за счет снятия внутренних напряжений и незначительное увеличение деформации при растяжении. В режиме обработки при постоянной плотности энергии деформация при растяжении растет прямо пропорционально плотности энергии и достигает 8.25 %. Отмечается, что режим обработки 15 Дж/см2, 150 мкс является недостаточным для растворения первичных кристаллов кремния, так как температура нагревания поверхностного слоя составляет 800 °С |
| Abstract (in another language): | The work presents the results of mechanical testing of samples of hypereutectic silumin before and after modification by the pulsed electronic beam of the submillisecond duration of exposure. The main feature of this type of processing is to melt the surface layer due to large heating rates (up to 10 9 f/s) and cooling (10 4 – 10 9 f/s). Processing was carried out in a stable processing mode (with a decrease in electron energy density) and with a constant density of the energy of the electron beam. When exposed to the surface in the mode of reducing the density of the energy of the beam of electrons, an increase in the strength of the strength due to the relief of internal stresses and a slight increase in the deformation during stretching. In processing mode with really energy density, the deformation during stretching grows directly to the amount of energy and reaches 8.25 %. It is noted that the processing mode is 15 J/cm2, 150 µs is insufficient to dissolve the primary silicon crystals, since the temperature of heating the surface layer is 800 °С. The hardness of the samples increases and reaches values up to 1.3 GPa. Thus, the pulse electronic bundle can be used to modify the surface of the hypereutectic silumin |
| Description: | Секция 3. Влияние излучений на структуру и свойства материалов = Section 3. Radiation Influence on the Structure and Properties of Materials |
| URI: | https://elib.bsu.by/handle/123456789/340597 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Sponsorship: | Работа выполнена при финансовой поддержке Российского научного фонда РНФ № 24-69-00074. |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2025. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 329-331.pdf | 110,58 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.