https://elib.bsu.by/handle/123456789/340468| Title: | Нагрузка полного отслаивания вакуумно-дуговых покрытий TiN, сформированных на различных подложках |
| Other Titles: | Load of Complete Peeling of Vacuum-ARC Tin Coatings Formed on Different Substrates / Kushnerou A.V., Konstatinov S.V., Shelkovaya T.V. |
| Authors: | Кушнеров, А. В. Константинов, С. В. Шелковая, Т. В. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2025 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом : материалы 16-й Междунар. конф., Минск, Беларусь, 22-25 сент. 2025 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2025. – С. 402-405. |
| Abstract: | Проведено исследование адгезионных свойств вакуумно-дуговых покрытий TiN, нанесенных на подложки из отожженной инструментальной стали 9ХС и твердых сплавов Т5К10 (TiC-Co) и ВК10 (WC-Co). Установлено, что исследуемые покрытия содержат фазу TiN с ГЦК решеткой и включения титана. Нанотвердость покрытий составила ≈ 29 ГПа. Показано, что нагрузка полного отслаивания (Lc3) покрытия TiN для случая подложек из твердых сплавов составляет 70-100 Н, что в 2.3-3.3 раз превышает Lc3 для стали 9ХС (30 Н). Сделано заключение, что высокий уровень нагрузки отслаивания для покрытий, сформированных на подложках из твердых сплавов, обусловлен их высокой твердостью, что предотвращает пластическую деформацию подложки в процессе скретч-тестирования. Структурная совместимость TiN с карбидной фазой TiC, содержащейся в твердом сплаве Т5К10, обеспечивает дополнительное увеличение Lc3 для покрытия TiN, сформированного на подложке из твердого сплава Т5К10 |
| Abstract (in another language): | The adhesive properties of TiN vacuum-arc coatings deposited on substrates of annealed 9XC tool steel and hard alloys T5K10 (TiC-Co) and WK10 (WC-Co) have been studied. It was established that the investigated coatings contain a TiN phase with a FCC lattice and titanium inclusions. The nanohardness of the coatings was ≈ 29 GPa. It is shown that the total peeling load (Lc3) of the TiN coating for the case of hard alloy substrates is 70-100 N, which is 2.3-3.3 times higher than Lc3 for 9XC steel (30 N). It is concluded that the high level of peeling load for coatings formed on hard alloy substrates is due to their high hardness, which prevents plastic deformation of the substrate during scratch testing. The structural compatibility of TiN with the TiC carbide phase contained in the T5K10 hard alloy provides an additional increase in Lc3 for the TiN coating formed on the T5K10 hard alloy substrate |
| Description: | Секция 4. Наноматериалы: формирование и свойства при воздействии излучений = Section 4. Nanomaterials: Formation and Properties under the Influence of Radiation |
| URI: | https://elib.bsu.by/handle/123456789/340468 |
| ISSN: | 2663-9939 (print) 2706-9060 (online) |
| Licence: | info:eu-repo/semantics/openAccess |
| Appears in Collections: | 2025. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 402-405.pdf | 128,75 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.