Межфазный синтез наночастиц магнетита с золотой оболочкой

Abstract

The original technologically simple method for synthesis of bifunctional Fe3O4/Au nanoparticles by the interphase reduction of a solution of chloroauric acid complex with quaternary ammonium compound in the organic phase containing a colloid solution of magnetite using sodium borohydride have been proposed. The principles of interphase synthesis and properties of prepared nanoparticles were investigated by TEM, optical spectroscopy, XRD, Mössbauer spectroscopy, IR-spectroscopy and TGA. The synthesized core-shell nanoparticles have a particle size of 12,8 nm with gold shell thickness of approximately 1,2 nm and exhibited a surface plasmon resonance peak at 590 nm. = Предложен оригинальный технологически простой способ получения бифункциональных наночастиц Fe3O4/Au межфазным восстановлением борогидридом натрия раствора комплекса золотохлористо-водородной кислоты с четвертичным аммониевым соединением в органической фазе, содержащей коллоидный раствор магнетита. Методами трансмиссионной электронной микроскопии, оптической спектроскопии, рентгенофазового анализа, мёссбауэровской спектроскопии, ИК-спектроскопии, термогравиметрического анализа исследованы закономерности межфазного синтеза и свойства полученных наночастиц. Синтезированные наночастицы состава ядро – оболочка диаметром 12,8 нм и золотой оболочки толщиной ~1,2 нм характеризуются поверхностным плазмонным резонансом при 590 нм.