https://elib.bsu.by/handle/123456789/208257| Title: | Сопротивление солевой коррозии деталей из жаропрочных сталей подвергнутых обработке сильноточными импульсными электронными пучками |
| Other Titles: | Salt corrosion resistance of refractory steel components treated with intense pulsed electron beams / V. A. Shulov, N. I. Fomin, V. I. Engelko, V. N. Kovalev, A. G. Paykin, A. F. Lvov |
| Authors: | Шулов, В. А. Фомин, Н. И. Энгелько, В. И. Ковалев, В. Н. Пайкин, А. Г. Львов, А. Ф. |
| Keywords: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Issue Date: | 2003 |
| Publisher: | Минск : БГУ |
| Citation: | Взаимодействие излучений с твердым телом: материалы V междунар. науч. конф., 6-9 окт. 2003 г., Минск. — Мн.: БГУ, 2003. — С. 320-322. |
| Abstract: | Исследованы поверхностные слои образцов и лопаток ГТД из сплава ВТ9 с эрозионностойким покрытием из ZrN полученным вакуумно-дуговым методом (15-20 мкм) и из сплава ЖС26НК с NiCrAIY покрытием (~100 мкм). Эти мишени подвергались облучению на ускорителе «Геза-2» по режимам, обеспечивающим интенсивный унос материала покрытия. Изучена кинетика абляции этих покрытий при облучении мишеней мощными импульсными электронными пучками при различных плотностях энергии в импульсе. Разработаны основы экологически чистых электронно-лучевых технологических процессов ремонта и восстановления свойств лопаток ГТД с различными видами защитных покрытий. |
| Abstract (in another language): | The objective of the present research is the critical analysis of test results, dedicated to the effect of electron-beam irradiation conditions upon the corrosion resistance of refractory steels under the thermocyciing conditions. The specimens produced of EP866sh and EP718ID steels by machining method are used as the study objects. The electron-beam treatment was realized by means of Gesa-1 accelerator. After irradiation some targets were subjected to vacuum annealing for 6 hours at their service temperature. Corrosion tests of initial and irradiated samples were performed under the following conditions: heating up to the operating temperature and then cooling in the sea water down to the room temperature. The target surface state prior to and after tests was studied by electron Auger spectroscopy, scanning electron microscopy and X-ray structural analysis. The test results showed that the corrosion resistance of samples, subjected to the electron-beam irradiation with the post-process vacuum annealing at the optimum conditions, could be increased by 200-300 %. |
| URI: | http://elib.bsu.by/handle/123456789/208257 |
| ISBN: | 985-445-236-0; 985-445-235-2 |
| Appears in Collections: | 2003. Взаимодействие излучений с твердым телом |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 320-322.pdf | 3,18 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.