Abstract

Fibrous carboxylic cation-exchanger has been prepared by acrylic acid grafting to the polypropylene fibers preliminarily exposed to γ irradiation of 60Co in air. A thermal stability of the cation-exchanger prepared has been studied by the combined thermal analysis and volumetry as well. The stability of the grafted fibers to a thermal oxidative destruction has been shown to decrease in the presence of iron (III). When a cross-linking co-monomer was used during the synthesis a reduced oxygen consumption rate has been determined, while oxidation induction period value being unchanged. The same peculiarities have been observed when hydroperoxide and peroxide compounds were decomposed. = Методами совмещенного термического анализа и волюмометрии исследована термическая стабильность волокнистого карбоксильного катионита, полученного прививкой акриловой кислоты полипропиленовым волокнам, облученным на воздухе γ-лучами 60Со. Показано, что в присутствии железа(III) устойчивость привитых волокон к термоокислительной деструкции снижается. Использование сшивающего сомономера при синтезе привитых волокон, а также разрушение пероксидных и гидропероксидных соединений вызывает снижение скорости поглощения кислорода, но не отражается на величине индукционного периода окисления.