Заглавие документа: | SYNTHESIS AND CHARACTERIZATION POLYMER COMPOSITES PREPARED BY LOW-TEMPERATURE POST-IRRADIATION POLYMERIZATION OF C2F4 IN THE PRESENCE OF GRAPHENE-LIKE MATERIAL |
Авторы: | Shulga, Y. M. Kiryukhin, D. P. Vasilets, V. N. |
Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
Дата публикации: | 2015 |
Аннотация: | Polymer polytetrafluoroethylene (PTFE)–microwave exfoliated graphene oxide (MEGO) composites containing up to 80 wt.% PTFE were prepared by low-temperature post-irradiation polymerization of C2F4 in the presence of the graphene-like material. Composites were characterized by elemental analysis, XPS, NMR, and DSC techniques. The melting point of PTFE in the composite (332.5 oC) was higher than that of pure PTFE by 8.8 oC. The measured values of the melting enthalpy (ΔHm=51.5 and 45.4 J/g) were used to calculate the extent of crystallinity in the PTFE and PTFE–MEGO composite (0.63 and 0.55, respectively). No - CF3 end groups typical of commercial PTFE have been detected in the PTFE–MEGO composites. |
URI документа: | http://elib.bsu.by/handle/123456789/120233 |
Располагается в коллекциях: | 2015. Взаимодействие излучений с твердым телом |
Полный текст документа:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
Shulga.pdf | 548,47 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.