Ориентация жидкокристаллического мономера полимерами с бензальдегидными группами

Abstract

The comparative experimental investigation of photocrosslinking of methacrylate polymer B-15 with benzaldehyde side groups and photoinduced alignment of LC monomer created by its surface has been performed. Almost coinciding exposure dependencies of gel fraction and quality parameter of alignment after rubbing allowed to consider the amplification of anchoring energy of the rubbed layer during its UV exposure as a result of progressive photocrosslinking. Alignment effects appearing upon linear-polarized irradiation are considerably weaker and they reach the saturation at sufficiently larger exposing dozes (depth of photoconversion). Observation of superposition of the photoalignment and the depressed rubbing alignment allows to suggest that the anisotropic surface deformation of the rubbed and exposed layer causes photoinduced amplification of its aligning ability. = Проведено сравнительное экспериментальное исследование фотосшивания слоев метакрилатного полимера с бензальдегидными боковыми группами B-15 и создаваемой их поверхностью фотоиндуцированной ориентации ЖК-мономера. Практическое совпадение экспозиционных зависимостей доли геля и параметра качества ориентации после натирания позволило связать рост энергии сцепления натертого слоя в ходе его УФ-облучения с развивающимся фотосшиванием. Ориентационные эффекты, возникающие при линейно-поляризованном облучении (фотоориентация), значительно слабее и достигают насыщения при существенно больших экспозиционных дозах (глубине фотоконверсии). Наблюдаемая при ослабленном ориентационном эффекте от натирания его суперпозиция с эффектом фотоориентации позволила сделать предположение об анизотропной поверхностной деформации натертого и облученного полимера как причине фотоиндуцированного усиления ориентирующих свойств.