Состояние золота в пленках SnO2-AU и In2O3-AU по данным оптической спектроскопии

Abstract

SnO2, In2O3, SnO2–Au and In2O3–Au (0,2–0,5 wt. % Au) fi lms obtained by sol-gel method were studied by optical spectroscopy. It has been established that gold is present in form of nanoparticles (Au0) with sizes < 2 nm and clusters after heating of the fi lms. These particles are stabilized by the interaction of gold with the oxide matrixes. The oxidation states of gold (Au+, Au3+) may be a boundary layer of (0Aum) particles on SnO2 and In2O3 oxides. High dispersity of Au particles after heating of the fi lms is caused by stabilization of gold clusters due to forming Sn–O–Au bonds in SnO2 –Au and In–Au bonds in In2O3–Au. = Методом оптической спектроскопии исследованы пленки SnO2, In2O3, SnO2−Au и In2O3−Au (0,2−0,5 мас. % Au), полученные золь-гель методом. Установлено, что после прогрева пленок золото присутствует в виде наночастиц (0Aum) с размерами < 2 нм и кластеров , которые стабилизируются благодаря взаимодействию золота с оксидной матрицей. Окисленные состояния золота (Au+, Au3+) может представлять собой граничный слой (0Aum) на оксидах SnO2 и In2O3. Высокая дисперсность частиц Au при прогреве обусловливается стабилизацией кластеров золота в результате образования связи Sn−O−Au в SnO2−Au и связи In−Au в In2O3−Au.