Влияние окисления на механизмы проводимости в нанокомпозитах FeCoZr-Al2O3

Abstract

Results of investigations of oxidation influence on the FeCoZr-Al2O3 nanocomposites conductivity mechanisms have been presented. Changing of the structural and phase composition of (Fe45Co45Zr10)x(Al2O3)100–x films deposited in argon and oxygen atmosphere has been analyzed as compared with the samples sputtered in pure argon. The absence of a percolation threshold in nanocomposites produced in argon + oxygen mixture was determined. Predominance of exponential conductivity type in FeCoZr-Al2O3 samples for the metallic phase concentration region of x = 35÷65 at. % was revealed. = Представлены результаты исследований влияния окисления на механизмы проводимости в нанокомпозитах FeCoZr-Al2O3. Проанализировано изменение структурных и фазовых свойств композитов (Fe45Cо45Zr10)x(Al2O3)100–x, синтезированных в атмосфере аргона и кислорода, по сравнению с образцами, полученными в атмосфере аргона. Зафиксировано, что синтез указанных композитов в кислородсодержащей среде приводит к исчезновению порога перколяции, т. е. препятствует формированию токопроводящей сети металлического типа. При этом во всем исследуемом диапазоне концентраций металлической фазы x = 35÷65 ат. % в нанокомпозитах преобладает экспоненциальный (активационный) тип проводимости.