https://elib.bsu.by/handle/123456789/233851| Заглавие документа: | Применение метода мгновенных ядерных реакций для изучения влияния Li на структурно-фазовое состояние быстрозатвердевшего сплава системы Al-Mg-Li |
| Другое заглавие: | Nuclear Reaction Analysis in Studying the Li Effect on Structure-Phase State of Rapidly Solidified Al-Mg-Li System Alloy / Iuliana Bushkevich, Vasiliy Shepelevich, Elke Wendler, Iya Tashlykova-Bushkevich, Mikalai Adzintsou, Marharyta Kacharha |
| Авторы: | Бушкевич, И. А. Шепелевич, В. Г. Wendler, E. Ташлыкова-Бушкевич, И. И. Адинцов, Н. В. Кочерга, М. В. |
| Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
| Дата публикации: | 2019 |
| Издатель: | Минск : БГУ |
| Библиографическое описание источника: | Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids : материалы 13-й Междунар. конф., Минск, Беларусь, 30 сент. – 3 окт. 2019 г. / редкол.: В. В. Углов (отв. ред.) [и др.]. – Минск : БГУ, 2019. – С. 505-507. |
| Аннотация: | Работа посвящена исследованию распределения лития по глубине быстрозатвердевших (БЗ) фольг авиационного алюминиевого сплава 1421, а также изучению влияния лития на структурно-фазовое состояние образцов при высокотемпературном отжиге с помощью метода мгновенных ядерных реакций, рентгеноструктурного анализа, а также метода измерения микротвердости материала. Установлено, что концентрация лития, входящего в состав оксида Li2O2, на контактирующей при кристаллизации с подложкой поверхности образцов возрастает в 4.2 раза и достигает 38.0 ат. % после отжига при 380°С в течение 1 ч. Обнаруженный эффект упрочнения БЗ фольг при повышении температуры изотермического отжига до 400°C объясняется выделением Li-содержащих метастабильных фаз S1(Al2LiMg) и X(Al(Mg, Sc, Zr, Li)x). |
| Аннотация (на другом языке): | This work presents an investigation of lithium distribution through the foil depth of rapidly solidified foils of aviation aluminium alloy 1421, as well as lithium effect on structure-phase state of samples at high-temperature annealing by means of nuclear reaction analysis, X-ray structure analysis and Vickers microhardness test method. In performed experiments, the 7 Li(p, α) 4 He reaction was applied for the measurement of lithium in the Al matrix. The nuclear reaction analysis accompanied by SIMNRA simulation was shown is favourable to investigate the lithium behaviour in foils up to the maximum observable depth of 22 μm. It was found that at the sample surface which is in contact with the substrate during its solidification the concentration of lithium as a component of Li2O2 oxide is increased in 4.2 times and reaches 38.0 at. % after annealing at 380°С during 1 h. While the oxide film of the as-cast foil surface mainly consists of Li2O2, MgO and Al2O3, the high-temperature annealing results in pronounced oxidation of the foil surface as well as decomposition of supersaturated solid solution with formation of Li-containing phases. The revealed effect of hardening of rapidly solidified foils at increasing temperature of the isothermal annealing up to 400°С after 20 min exposure is explained by the precipitation of Li-containing metastable S1(Al2LiMg) and X(Al(Mg, Sc, Zr, Li)x) phases. |
| Доп. сведения: | Секция 6. Современное оборудование и технологии = Section 6. Advances in Equipment and Technologies |
| URI документа: | http://elib.bsu.by/handle/123456789/233851 |
| ISSN: | 2663-9939 |
| Располагается в коллекциях: | 2019. Взаимодействие излучений с твердым телом = Interaction of Radiation with Solids |
Полный текст документа:
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| 505-507.pdf | 365,91 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.