Физико-химические свойства электродных материалов на основе La2NiO4±δ

Abstract

The solid solutions composition of La2Ni0,9Fe0,1O4 and La2Ni1–xCoxO4 (x = 0; 0,1; 0,2; 0,3) with spinel structure type of K2NiF4 were synthesized by glycine-nitrate method. The dependence of relative extension of sample, coefficient of thermal expansion (CTE) and electroconductivity of oxygen nonstoichiometry were determined. It was found the rise of substitute concentration increased the CTE value of samples. It was established that electroconductivity was raised for all compositions up to 940 K, then its value was decreased. The greatest values were typical for samples of composition La2Ni0,9Fe0,1O4 in the temperature interval 300÷1100 K. Also it was found the electrode materials interacted with solid electrolyte Bi1,5Y0,5O3 at 1100 K, and with solid electrolytes Ce0,9Gd0,1O1,95, Zr0,82Y0,10Mg0,08O1,87 at temperature of 1600 K. = Глицин-нитратным методом синтезированы твердые растворы составов La2Ni0,9Fe0,1O4 и La2Ni1–xCoxO4 (х = 0; 0,1; 0,2; 0,3) со структурой шпинели типа K2NiF4. Установлена зависимость относительного удлинения образцов, КТР и электропроводности от кислородной нестехиометрии. Рост концентрации заместителя увеличивает значения КТР образцов. Для всех составов до 940 К электропроводность возрастает, выше уменьшается. Наибольшие значения характерны в интервале 300÷1100 К для образцов состава La2Ni0,9Fe0,1O4. Электродные материалы взаимодействуют с твердыми электролитами (ТЭ) Bi1,5Y0,5O3 при 1100 К, а с Ce0,9Gd0,1O1,95, Zr0,82Y0,10Mg0,08O1,87 при 1600 К.