Полимерный композит - предшественник аморфного оксида железа (III)

Abstract

The composition phosphate cellulose (powder) – iron hydroxide with a various ratio of components is received. Thermogravimetric researches of a composition are carried out in an interval of temperatures 20÷70 °С. It is established, that thermal oxidizing transformations of a composition at annealing temperature of 500 °C result in reception X-ray amorphous iron hydroxide with preservation by it of the powder replica of the cellulose preсursor. The assumption is stated, that at thermal oxidizing decomposition of a cellulose phosphate composite occurs chemical modification of a surface formed oxide particles of iron by a layer of iron phosphate that interrupts their integration and crystallization. = Получена композиция фосфатцеллюлоза (порошковая) – гидроксид железа(III) с различным соотношением компонентов. Проведены термогравиметрические исследования композита в температурном интервале 20÷700 ○С. Установлено, что термоокислительные превращения композиции при температуре отжига 500 ○С приводят к получению рентгеноаморфного оксида железа с сохранением им порошковой фактуры целлюлозного предшественника. Предполагается, что при терморазложении фосфатцеллюлозного композита происходит химическая модификация поверхности образующихся оксидных частиц железа слоем фосфата железа, что препятствует их укрупнению и кристаллизации.