Генерация когерентных фононов в тонких пленках манганитов La0,67Ca0,33MnO3

Abstract

We have observed coherent optical phonon generation in thin La0,67Ca0,33MnO3 films deposed on SrTiO3 substrates using femtosecond optical pump-probe spectroscopy. The frequency of the coherent phonons is about 2,4 THz and is temperature independent within a temperature range of 140-165 K. while their amplitude falls down with decreasing temperature. A conclusion has been drawn that the generation of coherent phonons provides a sensitive detection method of charge ordered clusters within a ferromagnetic matrix. In the La0,67Ca0,33MnO3 films investigated the clusters have been induced by tensile stress developed in the film and are responsible for coherent oscilallations observed in the optical response. Методом накачки-зондирования фемтосекундными оптическими импульсами обнаружено возбуждение когерентных оптических фононов в тонких пленках La0,67Ca0,33MnO3, нанесенных на подложки из SrTiO3. Частота когерентных фононов составляет около 2,4 ТГц и не зависит от температуры в области 140-165 К, с понижением температуры их амплитуда уменьшается. Сделан вывод о том, что возбуждение когерентных фононов является эффективным методом обнаружения кластеров с зарядовым упорядочением в ферромагнитной матрице. В исследованных пленках La0,67Ca0,33MnO3, данные кластеры образуются под воздействием деформационных напряжений растяжения в пленке и приводят к появлению когерентных колебаний в оптическом отклике.