Заглавие документа: | THE TRANSMITTANCE TEMPERATURE DEPENDENCE AND SPIN GLASS-LIKE BEHAVIOR IN THE NANOCOMPOSITE Fe – In2O3 THIN FILMS |
Авторы: | Tambasov, I. A. Platunov, M. S. Ovchinnikov, S. G. |
Тема: | ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика |
Дата публикации: | 2015 |
Аннотация: | The ferromagnetic Fe-In2O3 nanocomposite thin film has been synthesized by the thermite Fe2O3 + In → Fe-In2O3 reaction. The transmittance (400 – 1100 nm) was measured at temperatures from 320 to 5 K. It was found that the transmittance increases when temperature decreases. For wavelength 600, 700, 800, 900 and 1000 nm maximum change of transmittance was ~ 3.2, 4.2, 4.8, 5.1 and 5.4 %, respectively. From transmittance spectra, spin glass-like behavior was observed near ~ 36 K and confirmed by magnetization measurements. The Verwey transition was identified at ~ 127 K by magnetization measurements. We have shown direct relationship between transmittance and magnetization of nanocomposite Fe – In2O3 thin film near ~ 36 K and give proposed possible mechanism this phenomena. |
URI документа: | http://elib.bsu.by/handle/123456789/120081 |
Располагается в коллекциях: | 2015. Взаимодействие излучений с твердым телом |
Полный текст документа:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
Tambasov.pdf | 551,4 kB | Adobe PDF | Открыть |
Все документы в Электронной библиотеке защищены авторским правом, все права сохранены.